Film Faced Plywood Film Faced Plywood,Film Faced Plywood,Film Faced Plywood,Film Faced Plywood,Film Faced Plywood,Melamine Laminated Plywood Melamine Laminated Plywood,Melamine Laminated Plywood,18mm Melamine Laminated Plywood,melamined board, melamined plywood, melamined MDF,1220x2440x18mm melamined paper covered on plywood manufacturer Melamine Laminated Plywood,Structural F17 Formply 1200*1800*17mm,Film Faced Plywood,F17 formply,Film Faced Plywood Structural F17 formply 1200*1800*17mm,F17 Formply 1200*1800*17mm,Film Faced Plywood Structural F17 formply 1200*1800*17mm,Formply F17 construction F17 Formply,construction F17 Formply,construction F17 Formply,construction F17 Formply,construction F17 Formply

AS6669 F17 Formply 1200*1800*17mm Film Faced Plywood F17 formply Formwork plywood

Film Faced Plywood
AS6669 F17 Formply 1200*1800*17mm Film Faced Plywood F17 formply Formwork plywood
F17-11
AS6669 F17 Formply 1200*1800*17mm

Size: 1200*1800*17mm;
Core material: Eucalyptus;
Glue: Phenolic glue A bond (72 hours in boiling water);
Surface: Dynea black film, off-finish Class 2
Quantity
Film Faced Plywood

F17 formply Film Faced Plywood Structural Formply is used in construction industry for forming concrete. F17 formply is made with a bond glue,hardwood core and poplar veneer faces with a high density overlay resin impregnated finish. Perfect for use in concrete formwork and can be used several times. Usually, used in outdoor environment and exposed to external weather conditions, rain, sun light, heat from concrete being formed.
 F17 formply Film Faced Plywood
Recommended for decks, retaining walls, bridges, culvert construction, building slabs, civil engineering projects etc


F17 formply Film Faced Plywood

Size: 1220*1800mm

Thickness: 17mm
Core material: hardwood, pine, etc
Glue: phenolic glue A bond (72 hours in boiling water)
Face/Back: Dynea film, black/brown film, Off-finish Class 2
Moisture Content: 6-10%
Application: concrete formwork, construction, wagon building, etc;

Characteristics - High strength and stiffness to weight ratio; high dimensional stability; high panel shear; chemical resistance.